摘要：随着我国经济的高速发展，路桥施工也得到了全面的发展。在路桥施工中通常使用混凝土作为重要的施工材料，但是由于混凝土自身的原因，造成了路桥施工中经常会有裂缝问题的发生。路桥施工中一旦出现裂缝，如果不进行及时有
关键词：路桥工程；裂缝；原因；防治措施
Abstract: With China's rapid economic development, road and bridge construction has been all-round development. Commonly used in road and bridge construction concrete as a construction material, but due to the concrete, resulting in road and bridge construction, there is often a crack problem occurred. Once the cracks in road and bridge construction, if not timely and effective control will he serious consequences. For cracks in the road and bridge construction process, from raw material ratio, the chemical reaction of concrete construction impact analysis of the causes of cracks and fracture prevention measures targeted to guide practice, to ensure the quality of roads and bridges projects.Key words: road and bridge projects; cracks; reasons; prevention measures
2095-2104（2012）10-0020-02
1裂缝产生的原因
路桥施工过程中产生裂缝的原因之一是由静荷载所引起的裂缝和动荷载的应力引起的裂缝。这两种原因都属于结构性裂缝，主要是由于钢筋混凝土结构的承载力不足所引起的。如果发生结构性裂缝说明桥梁的强度不足，在桥梁运营中潜藏巨大的结构性危险。路桥施工过程中也会产生由于变形引起的非受力性裂缝。非受力性裂缝主要是由于钢筋混凝土结构内部自身应力发生形变。从目前的工程实践经验来说，非受力性裂缝约占路桥施工过程中产生裂缝的80%以上，结构性裂缝只占20%左右。裂缝产生的原因为原材料配比，混凝土化学反应，温度等外部自然环境的影响，施工的影响，地基础变形五个方面产生。
1．1原材料配比不合理
混凝土主要材料是水泥、拌和骨料、水、砂及外加剂按特定比例混合组成。如果混凝土所采用的原材料品质不合格，会导致钢筋混凝土结构内出现裂缝。在选择粗细集料时，必须确保含泥量的标准。如果含泥量过高会造成混凝土浇筑后收缩增大，混凝土强度降低，还会使混凝土发生渗水等问题。保含泥量过高主要体现在混凝土干燥后，表面会产生无规则的网状裂缝。拌和用水的选择，外加剂的添加都要结合工程实际情况。拌和用水和外加剂一般都含有一定比例的氯化物等杂质，这些化学物质会锈蚀钢筋，降低桥梁的承载能力。如果拌和用水和外加剂的碱含量过高就会与骨料发生反应，对结构产生影响。水泥的等级也是影响裂缝的原因之
混凝土收缩裂缝的主要表现为表面出现裂缝，裂缝的宽度一般较为细小，无规则的龟裂状。混凝土在不受外力的情况下，会发生收缩这种自发变形。当受到外部约束作用时，混凝土就会产生拉应力导致其开裂。这种体积变形主要发生在硬化初期和后期，硬化初期的水泥在凝固结硬过程中体积发生变化，后期是内部自由水分蒸发导致的干缩变形。
水泥水化热也是发生混凝土收缩裂缝原因之一。水泥在水化过程中会放出大量的热，由于散热不均匀，使混凝土内部的温度一般比表面高很多。尤其对于大型的混凝土结构来讲，温差会更加严重。混凝土内部和表面的散热导致的温度梯度，使混凝土内部发生压应力，表面却是拉应力，当作用力超过混凝土承受的极限时，表面就会产生裂缝。
1．3温度等外部自然环境的影响
混凝土也具有热胀冷缩的性质。外界气候的变动会促使混凝土结构产生裂缝。桥梁部分主体结构受到太阳曝晒后，曝晒部分和阴凉部分呈非线形的温度梯度。桥梁本身的约束作用和温度导致的局部拉应力，都促使混凝土结构出现裂缝。混凝土结构内部受到浇筑温度，水泥水化释放的温度和自然条件对其产生的温度的影响，如果外界环境温度发生巨大变动就会增大混凝土结构的内外温度梯度，产生温度应力，引发混凝土结构局部开裂。严冬天气引起的冻胀裂缝。在大气气温低于0℃的情况下，游离在混凝土结构中的水转变成冰，混凝土体积膨胀不均匀，并且由于混凝土未完全粘合强度较低，就会有裂缝出现。
1．4不正确的施工的影响
混凝土在施工过程中过分振动搅拌，模板、垫层未吸收足够的水分，这些原因都会引起凝缩裂缝。混凝土在浇捣到建筑体后，抹干压光时间过久会使细骨料浮至表面，形成水泥浆层。水泥浆含有大量的氢氧化钙会与空气中二氧化碳发生化学反应，导致混凝土板面体积收缩出现龟裂现象。由于一般施工都是露天作业，钢筋都会发生一定的锈蚀，这会导致混凝土结合部充分发生裂缝。由于施工是分段进行的，混凝土结构一般会分段进行浇筑，如果处理不好接头部位的浇筑，在新旧混凝土之间比较容易出现裂缝。
1．5地基沉降引起的裂缝
桥梁的地基竖向受力不均发生沉降，混凝土结构间产生额外应力，当超出其自身的抗拉能力，裂缝就会产生。
2施工过程裂缝的防治措施
优化混凝土材料的配合比例，对其主要材料水泥的用量要严格控制。从目前的施工实践技能可以得出合理原材料配合比例是防止裂缝出现的关键。针对混凝土要求的强度等级，充分考虑材料质量会引发结构变动，按照施工条件的差异，设计出一份合理的混凝土材料的配合比例。由于施工现场材料使用，环境变化会和计划量出现不一致，施工单位要根据施工现场的实际情况，及时调整混凝土材料的配合比例，有效地防止裂缝的产生。
钢筋施工质量好坏直接影响到整个工程质量。确保钢筋施工质量，首先得确保钢筋在排布时的间距合理均匀，设计好钢筋接头位置排布。合理设置保护层垫块位置和间距，用统一垫块有效固定。应根据负筋直径设置足够的钢筋马蹬，以防止负筋踩下不能上提复位。审核支架和模板等专项方案，确保支架和模板的拉伸刚度，应力强度，结构稳定性符合要求。模板的接缝处要严密焊接，不能出现漏浆现象。标示浇筑后的立柱高度，确保混凝土结构的整体高度和平整度。浇筑前，对支架结构、模板、钢筋结构、保护层垫进行认真检查，确保它们符合设计要求后才可浇筑。
源于：论文的格式要求www.udooo.com
效的控制，将会产生严重的后果。本文主要针对路桥施工过程中产生的裂缝，从原材料配比、混凝土化学反应、施工影响等几个方面分析了裂缝产生的原因，并针对性地提出了相应的裂缝防治措施，以指导实践，保证道路桥梁工程质量。关键词：路桥工程；裂缝；原因；防治措施
Abstract: With China's rapid economic development, road and bridge construction has been all-round development. Commonly used in road and bridge construction concrete as a construction material, but due to the concrete, resulting in road and bridge construction, there is often a crack problem occurred. Once the cracks in road and bridge construction, if not timely and effective control will he serious consequences. For cracks in the road and bridge construction process, from raw material ratio, the chemical reaction of concrete construction impact analysis of the causes of cracks and fracture prevention measures targeted to guide practice, to ensure the quality of roads and bridges projects.Key words: road and bridge projects; cracks; reasons; prevention measures
2095-2104（2012）10-0020-02
1裂缝产生的原因
路桥施工过程中产生裂缝的原因之一是由静荷载所引起的裂缝和动荷载的应力引起的裂缝。这两种原因都属于结构性裂缝，主要是由于钢筋混凝土结构的承载力不足所引起的。如果发生结构性裂缝说明桥梁的强度不足，在桥梁运营中潜藏巨大的结构性危险。路桥施工过程中也会产生由于变形引起的非受力性裂缝。非受力性裂缝主要是由于钢筋混凝土结构内部自身应力发生形变。从目前的工程实践经验来说，非受力性裂缝约占路桥施工过程中产生裂缝的80%以上，结构性裂缝只占20%左右。裂缝产生的原因为原材料配比，混凝土化学反应，温度等外部自然环境的影响，施工的影响，地基础变形五个方面产生。
1．1原材料配比不合理
混凝土主要材料是水泥、拌和骨料、水、砂及外加剂按特定比例混合组成。如果混凝土所采用的原材料品质不合格，会导致钢筋混凝土结构内出现裂缝。在选择粗细集料时，必须确保含泥量的标准。如果含泥量过高会造成混凝土浇筑后收缩增大，混凝土强度降低，还会使混凝土发生渗水等问题。保含泥量过高主要体现在混凝土干燥后，表面会产生无规则的网状裂缝。拌和用水的选择，外加剂的添加都要结合工程实际情况。拌和用水和外加剂一般都含有一定比例的氯化物等杂质，这些化学物质会锈蚀钢筋，降低桥梁的承载能力。如果拌和用水和外加剂的碱含量过高就会与骨料发生反应，对结构产生影响。水泥的等级也是影响裂缝的原因之
一、一般水泥的等级、细度、早强都会影响混凝土结构。
1．2混凝土发生化学反应混凝土收缩裂缝的主要表现为表面出现裂缝，裂缝的宽度一般较为细小，无规则的龟裂状。混凝土在不受外力的情况下，会发生收缩这种自发变形。当受到外部约束作用时，混凝土就会产生拉应力导致其开裂。这种体积变形主要发生在硬化初期和后期，硬化初期的水泥在凝固结硬过程中体积发生变化，后期是内部自由水分蒸发导致的干缩变形。
水泥水化热也是发生混凝土收缩裂缝原因之一。水泥在水化过程中会放出大量的热，由于散热不均匀，使混凝土内部的温度一般比表面高很多。尤其对于大型的混凝土结构来讲，温差会更加严重。混凝土内部和表面的散热导致的温度梯度，使混凝土内部发生压应力，表面却是拉应力，当作用力超过混凝土承受的极限时，表面就会产生裂缝。
1．3温度等外部自然环境的影响
混凝土也具有热胀冷缩的性质。外界气候的变动会促使混凝土结构产生裂缝。桥梁部分主体结构受到太阳曝晒后，曝晒部分和阴凉部分呈非线形的温度梯度。桥梁本身的约束作用和温度导致的局部拉应力，都促使混凝土结构出现裂缝。混凝土结构内部受到浇筑温度，水泥水化释放的温度和自然条件对其产生的温度的影响，如果外界环境温度发生巨大变动就会增大混凝土结构的内外温度梯度，产生温度应力，引发混凝土结构局部开裂。严冬天气引起的冻胀裂缝。在大气气温低于0℃的情况下，游离在混凝土结构中的水转变成冰，混凝土体积膨胀不均匀，并且由于混凝土未完全粘合强度较低，就会有裂缝出现。
1．4不正确的施工的影响
混凝土在施工过程中过分振动搅拌，模板、垫层未吸收足够的水分，这些原因都会引起凝缩裂缝。混凝土在浇捣到建筑体后，抹干压光时间过久会使细骨料浮至表面，形成水泥浆层。水泥浆含有大量的氢氧化钙会与空气中二氧化碳发生化学反应，导致混凝土板面体积收缩出现龟裂现象。由于一般施工都是露天作业，钢筋都会发生一定的锈蚀，这会导致混凝土结合部充分发生裂缝。由于施工是分段进行的，混凝土结构一般会分段进行浇筑，如果处理不好接头部位的浇筑，在新旧混凝土之间比较容易出现裂缝。
1．5地基沉降引起的裂缝
桥梁的地基竖向受力不均发生沉降，混凝土结构间产生额外应力，当超出其自身的抗拉能力，裂缝就会产生。
2施工过程裂缝的防治措施
优化混凝土材料的配合比例，对其主要材料水泥的用量要严格控制。从目前的施工实践技能可以得出合理原材料配合比例是防止裂缝出现的关键。针对混凝土要求的强度等级，充分考虑材料质量会引发结构变动，按照施工条件的差异，设计出一份合理的混凝土材料的配合比例。由于施工现场材料使用，环境变化会和计划量出现不一致，施工单位要根据施工现场的实际情况，及时调整混凝土材料的配合比例，有效地防止裂缝的产生。
钢筋施工质量好坏直接影响到整个工程质量。确保钢筋施工质量，首先得确保钢筋在排布时的间距合理均匀，设计好钢筋接头位置排布。合理设置保护层垫块位置和间距，用统一垫块有效固定。应根据负筋直径设置足够的钢筋马蹬，以防止负筋踩下不能上提复位。审核支架和模板等专项方案，确保支架和模板的拉伸刚度，应力强度，结构稳定性符合要求。模板的接缝处要严密焊接，不能出现漏浆现象。标示浇筑后的立柱高度，确保混凝土结构的整体高度和平整度。浇筑前，对支架结构、模板、钢筋结构、保护层垫进行认真检查，确保它们符合设计要求后才可浇筑。